Shinde S.S.1*
1Department of Physics, A.S.C. College, Naldurg, 413 602, India.
* Corresponding Author : sureshshinde186@gmail.com
Received : - Accepted : - Published : 15-06-2010
Volume : 1 Issue : 1 Pages : 12 - 14
J Electron Electr Eng 1.1 (2010):12-14
Spinel ferrites with general formula Co0.7+x Zn0.3 Six Fe2-2x O4 (for x = 0.0 to 0.4) were prepared by standard double sintering ceramic method. Electrical properties of the present spinel system were studied by means DC and AC resistivity measurements. Both DC resistivity rdc and AC resistivity rac are found to increase with increase in Si concentration from x = 0.0 to 0.1 and then they decrease with increase in Si concentration from x = 0.2 to 0.4. AC resistivity rac of all the samples is found to increase at lower temperature and then it decreases with increase in temperature.
[1] B.P. Ladgaonkar, C.B. Kolekar, P. N.
Vasambekar, A.S.Vaingankar, Ind.
J.Eng. Mater. Sci. 7 (2000) 419.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[2] A.S. Vaingankar, S.G. Kulkarni, M.S.
Sagare J. Phys. France 7 (1997) C 1
– 155.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[3] E.J.W. Verwey, P.W. Haaijmann, E.C.
Romeyn, G.M.Van Oosterhont,
Philips Res. Rep. 5 (1950) 173.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[4] S.S. Shinde, K.M. Jadhav, Mater Lett.
37(1998) 63-67.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[5] Van Uitert L.C. Proc. IRE (USA), 1294
(1956)1303.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[6] A.B. Devale, D.K. Kulkarni, J. Pure and
Appl. Phys. 16(1978) 697.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[7] R. Satyanarayana, S.R. Murthy, T.S.
Rao and M.D. Rao, J. Less.
Commun. Metals, 86 (1982) 115.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus
[8] R.H.J. Waldron, Appi. Phys. (USA),
43(1972)1186.
» CrossRef » Google Scholar » PubMed » DOAJ » CAS » Scopus